With the aim of understanding failure modes in the peeling of silicone-based adhesive joints and, in particular, the occurrence of adhesive or cohesive failure, an experimental campaign has been conducted by considering plastic substrates with different surface roughness. A flexible strip has been bonded onto such substrates using a silicone adhesive, by controlling its thickness. Peeling tests with 90° and 180° peeling angle configurations have been performed and the effect of joint parameters, such as surface roughness and adhesive thickness, onto the adhesion energy and the failure mode are herein discussed in detail. Experimental results show that the failure mode varies in each peeling test configuration such that in the case of 180° peeling test there is mainly cohesive failure, while for 90° peeling angle, a combination of adhesive and cohesive failure occurs. Moreover, due to the presence of different failure modes in each peeling configuration, the substrate roughness can increase the adhesion energy only in 90° peeling tests.

Mechanical characterization and failure modes in the peeling of adhesively bonded strips from a plastic substrate

Hamed Zarei
Investigation
;
Maria Rosaria Marulli
Investigation
;
Marco Paggi
Investigation
;
2022-01-01

Abstract

With the aim of understanding failure modes in the peeling of silicone-based adhesive joints and, in particular, the occurrence of adhesive or cohesive failure, an experimental campaign has been conducted by considering plastic substrates with different surface roughness. A flexible strip has been bonded onto such substrates using a silicone adhesive, by controlling its thickness. Peeling tests with 90° and 180° peeling angle configurations have been performed and the effect of joint parameters, such as surface roughness and adhesive thickness, onto the adhesion energy and the failure mode are herein discussed in detail. Experimental results show that the failure mode varies in each peeling test configuration such that in the case of 180° peeling test there is mainly cohesive failure, while for 90° peeling angle, a combination of adhesive and cohesive failure occurs. Moreover, due to the presence of different failure modes in each peeling configuration, the substrate roughness can increase the adhesion energy only in 90° peeling tests.
2022
Silicone adhesives, surface roughness, fracture mechanics, peel test, adhesion energy, failure mode
File in questo prodotto:
File Dimensione Formato  
RevisedManuscript_MAMS.pdf

accesso aperto

Descrizione: Preprint of the article
Tipologia: Documento in Pre-print
Licenza: Creative commons
Dimensione 929.54 kB
Formato Adobe PDF
929.54 kB Adobe PDF Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.11771/17266
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 4
social impact